![Author ORCID: We display the ORCID iD icon alongside authors names on our website to acknowledge that the ORCiD has been authenticated when entered by the user. To view the users ORCiD record click the icon. [opens in a new tab]](https://chemrxiv.org/engage/assets/public/chemrxiv/images/logos/orcid.png)
Abstract
The present study investigates the mechanical and corrosion properties of reinforced 6061-T6 Aluminum samples after friction stir processing. Three different composites are fabricated: one without any powder and the others with micrometer and nanometer alumina powder ({Al}_2O_3) as reinforcing particles. The hardness, tensile, and Potentiodynamic polarization tests are performed to compare the new samples with the base metal. The results show that friction stir processing has increased the tensile and ultimate strength of the composites by an average of 181 % compared to the base metal. The strength of the composites with additives is significantly affected by the size of the particles. The hardness of the processed samples has also increased compared to the base metal by 200 %. Despite these enhancements, corrosion resistance of new samples has decreased, which can be due to the numerous dislocations in the stress-induced stir zone, creating lattice deformations and causing the breakdown of the passive protective layer. The analysis of fracture surface topography through a Fractography method revealed a specific anaglyph consisting of dimples of various shapes, sizes, and dispersion and further confirmed the tensile test results.